EGP-PP80 filler masterbatch

EGP-PP80 is a highly filled calcium carbonate filler masterbatch containing fine pure CaCO3 in polypropylene resin and special additives.

This filler masterbatch is intended to be added into polyolefin resins during extrusion, injection or blow molding to displace a portion of the resin, improve properties, cut costs.

Adding ratio is normally in the range of 20 to 40% (or even higher in some applications) depending on the particular product and processing conditions.

Suitable applications

Basic specification

Property

Test Method

Unit

Result

PP & Additive

%

20 ± 1

Shape

Granule

mm

2-3mm

Density

ASTM D1505

g/cm3

1,60g/1cm3

Moisture

ASTM D644

%

<0,2%

CaCO3 Percentage

%

80 ± 1

CaCo3 Particle Size (D50)

Malvern Mastersizer 3000E

µ

2.5 ± 0.3

EGP-PP82 filler masterbatch

EGP-PP82 is a highly filled calcium carbonate filler masterbatch containing fine pure CaCO3 in polypropylene resin and special additives.

This filler masterbatch is intended to be added into polyolefin resins during extrusion, injection or blow molding to displace a portion of the resin, improve properties, cut costs.

Adding ratio is normally in the range of 20 to 40% (or even higher in some applications) depending on the particular product and processing conditions.

Suitable applications

Basic specification

Property

Test Method

Unit

Result

PP & Additive

%

18 ± 1

Shape

Granule

mm

2-3mm

Density

ASTM D1505

g/cm3

1,60g/1cm3

Moisture

ASTM D644

%

<0,2%

CaCO3 Percentage

%

82 ± 1

CaCo3 Particle Size (D50)

Malvern Mastersizer 3000E

µ

2.5 ± 0.3

EGP-PP84 filler masterbatch

EGP-PP84 is a highly filled calcium carbonate filler masterbatch containing fine pure CaCO3 in polypropylene resin and special additives.

This filler masterbatch is intended to be added into polyolefin resins during extrusion, injection or blow molding to displace a portion of the resin, improve properties, cut costs.

Adding ratio is normally in the range of 20 to 40% (or even higher in some applications) depending on the particular product and processing conditions.

Suitable applications

Basic specification

Property

Test Method

Unit

Result

PP & Additive

%

16 ± 1

Shape

Granule

mm

2-3mm

Density

ASTM D1505

g/cm3

1,60g/1cm3

Moisture

ASTM D644

%

<0,2%

CaCO3 Percentage

%

84 ± 1

CaCo3 Particle Size (D50)

Malvern Mastersizer 3000E

µ

2.5 ± 0.3

EGP-PP01TM filler masterbatch

EGP-PP01TM is a highly filled calcium carbonate filler masterbatch containing fine pure CaCO3 in polypropylene matrix and special additives.

This filler masterbatch is intended to be added into polyolefin resins during extrusion, injection or blow molding to displace a portion of the resin, improve properties, cut costs.

Applicable for: PP non-woven fabric

Basic specification

Property

Test Method

Unit

Result

PP & Additive

%

21 ± 1

Shape

Granule

mm

2-3mm

Density

ASTM D1505

g/cm3

1,60g/1cm3

Moisture

ASTM D644

%

<0,2%

CaCO3 Percentage

%

79 ± 1

CaCo3 Particle Size (D50)

Malvern Mastersizer 3000E

µ

2.5 ± 0.3